Composite Comparison
 |
 |
 |
 |
|
Tetric EvoCeram® |
Tetric EvoFlow® |
Tetric EvoCeram® Bulk Fill |
Tetric EvoFlow® Bulk Fill |
|
| Buy Now | Buy Now | Buy Now | Buy Now |
Features
| Type | Nano-hybrid sculptable | Nano-hybrid flowable | Nano-hybrid 4mm sculptable | Nano-hybrid 4mm flowable |
| Shades | 14 Enamel (Body) 4 Dentin 4 Bleach |
8 Enamel (Body) 3 Dentin 3 Bleach |
3 Universal Shades (IVA, IVB, IVW) |
3 Universal Shades (IVA, IVB, IVW) |
| Filler % | ||||
| Weight | 75-76; 79-80 Bleach | 57.5 | 76-77 | 68.2 |
| Volume | 53-55; 60-61 Bleach | 30.7 | 53-54 | 46.4 |
| Particle Size (nm) | 40 - 3000 | 40 - 3000 | 40 - 3000 | 100 - 3000 |
| Mean Particle Size (nm) | 550 | 550 | 550 | 500 |
| Contains Ivocerin® |
Indication
| Deciduous Teeth | ||||
| Anterior (Class III, IV) | ||||
| Posterior (Class I, II) | ||||
| Class V | ||||
| Initial layer under Class I to V restorations | ||||
| Small restorations of all types | ||||
| Correction of tooth position/shape | ||||
| Splinting of mobile teeth | ||||
| Direct veneers | ||||
| Extended fissue sealing in molars/premolars | ||||
| Repair of composite/ceramic veneers | ||||
| Build-ups (attachments) for transparent, removable Invisalign® orthodontic retainers | ||||
| Blocking out undercuts | ||||
| Reconstructive build-up | ||||
| Adhesive cementation of light -transmissive indirect composite and ceramic restorations |
Physical Properties
| Flexural Strength (MPa) | 120 | 114 | 120 | |
| Flexural Modulus | 10000 | 5100 | 10000 | |
| Water Absorbtion (µg/mm3) | 21.2 | 21 | 21.1 | |
| Water Solubility (µg/mm3) | <1.0 | 0.1 | <1.0 | |
| Radiopacity (% Al) | 400; 200 Bleach I; 300 Bleach L, M, XL | 360; 250 Bleach I; 280 Bleach L, M, XL | 260 | |
| Depth of Cure (mm) | >1.5mm | >2.0 | 4 | 4 |
| Compressive Strength (MPa) | 250 | 260 | ||
| Translucency (%) | 6.5-20 | 6-30 | 15-17 | 9.8 |
| Vickers Hardness (MPa) | 250 | 260 | ||
| Working Time (sec) | 210 | 200 | 280 | |
| Volumetric Shrinkage (%) | 1.6 | 4.2 | 1.96 | 3.5 |
| Shrinkage Stress (MPa) | 1.4 |